Despite the increased public awareness and professional concern over the use of mercury in dental amalgam, only a few research groups have devoted considerable effort to determining the ultimate exposure and biological effects of this element. Therefore, many significant and imperative questions remain unanswered. The importance of this issue lies in the fact that approximately 80% of all posterior restorations are made from this material. The goal of the original research proposal was to systematically investigate the quantity, rate and mechanisms of mercury release from dental amalgams and their constituent phases by dissolution and evaporation. The overall goal of the present proposal is to continue this effort in order to establish maximum values for the level of exposure for dental patients and personnel to mercury from dental amalgams. In addition, further information on the rat, mechanism and chemical form of mercury released from amalgam will be obtained. A gold film mercury analyzer (Jerome 411) will be used to quantitate the vaporization of mercury from liquid mercury, amalgams and amalgam phases through aqueous solutions, as is expected to occur in vivo. The effects of corrosion and fatigue loading on mercury vapor release from amalgam will also be studied. In addition, the total amount of mercury vapor generated during trituration, placement, polishing and removal of amalgam will be quantitated in a closed system with the vapor analyzer, in order to determine the ultimate exposure to both patient and dental personnel. Atomic absorption spectroscopy will be used to quantitate the solubility limits and dissolution rate of mercury in water, saline and an artificial saliva. In addition, this technique will be employed to determine the total amount of mercury, as well as silver, copper, tin and zinc, dissolving from amalgam immersed in a flowing, continuously replenished solution, as would be encountered in vivo. Finally, the rate of formation and composition of the surface film forming on amalgam and its phases in air and saline will be determined by x-ray photoelectron spectroscopy, since this film has been shown to retard mercury emission. It is believed that the present study will more completely evaluate the mechanisms of release, as well as quantitate the total amount of mercury that the dental patient and personnel may be exposed to on a routine basis.

Agency
National Institute of Health (NIH)
Institute
National Institute of Dental & Craniofacial Research (NIDCR)
Type
Research Project (R01)
Project #
2R01DE007644-04
Application #
3221318
Study Section
Oral Biology and Medicine Study Section (OBM)
Project Start
1986-03-01
Project End
1994-03-31
Budget Start
1989-04-01
Budget End
1990-03-31
Support Year
4
Fiscal Year
1989
Total Cost
Indirect Cost
Name
Texas A&M Baylor College of Dentistry
Department
Type
Schools of Dentistry/Oral Hygn
DUNS #
City
Dallas
State
TX
Country
United States
Zip Code
75246
Koike, M; Ferracane, J L; Adey, J D et al. (2004) Initial mercury evaporation from experimental Ag-Sn-Cu amalgams containing Pd. Biomaterials 25:3147-53
Koike, Marie; Ferracane, Jack L; Fujii, Hiroyuki et al. (2003) Evaluation of the amalgamation reaction of experimental Ag-Sn-Cu alloys containing Pd using a mercury plating technique. Dent Mater J 22:280-91
Okabe, T; Elvebak, B; Carrasco, L et al. (2003) Mercury release from dental amalgams into continuously replenished liquids. Dent Mater 19:38-45
Ohmoto, K; Nakajima, H; Ferracane, J L et al. (2000) Mercury evaporation from amalgams with varied mercury contents. Dent Mater J 19:211-20
Ferracane, J; Adey, J; Wiltbank, K et al. (1999) Vaporization of Hg from Hg-in amalgams during setting and after abrasion. Dent Mater 15:191-5
Nakajima, H; Wataha, J C; Rockwell, L C et al. (1997) In vitro cytotoxicity of amalgams made with binary Hg-In liquid alloys. Dent Mater 13:168-73
Nakajima, H; Akaiwa, Y; Hashimoto, H et al. (1997) Surface characterization of amalgam made with Hg-In liquid alloy. J Dent Res 76:610-6
Okabe, T; Ohmoto, K; Nakajima, H et al. (1997) Effect of Pd and In on mercury evaporation from amalgams. Dent Mater J 16:191-9
Nakajima, H; Lorenzana, E; Ferracane, J L et al. (1996) Initial mercury evaporation from amalgams made with in-containing commercial alloys. Dent Mater J 15:168-74
Horasawa, N; Nakajima, H; Ferracane, J L et al. (1996) Cyclic voltammetry of dental amalgams. Dent Mater 12:154-60

Showing the most recent 10 out of 22 publications