Dental crowns and bridges are usually constructed by applying an esthetic porcelain veneer to a strong core. Ceramic core materials, such as zirconia and lithium disilicate, are currently favored for their ease of fabrication and for their strength. While porcelain chipping and fractures are observed in all types of veneered dental prostheses, they are particularly prevalent in porcelain-veneered zirconia. The high chipping/fracture rate is due predominantly to residual stresses introduced by the high-temperature veneering process. However, comprehensive knowledge of key material, design, and processing parameters that govern residual stresses remains obscure. The long-term goal of this project is to improve the fracture resistance of porcelain-veneered prostheses through the reduction of deleterious residual tensile stresses, in conjunction with superior design of a graded veneer/core interface. Accordingly, the overall objectives in this application are to develop a rigorous viscoelastic graded finite element method to guide the design of next-generation fracture-resistant porcelain- veneered ceramic prostheses, and to use clinically relevant fracture mechanics test methods to validate finite element model predictions. The central hypothesis is that the incidence of chipping and fracture of porcelain- veneered ceramics can be reduced to the levels seen in porcelain-fused-to-metal prostheses, through the optimization of material, design, and processing parameters. This hypothesis is formulated on the basis of preliminary results produced in the applicants' laboratories. To test this hypothesis, we will pursue two specific aims: (1) Develop a rigorous viscoelastic graded finite element model, and use this model to optimize the residual stress profile in anatomically-correct porcelain-veneered prostheses through the tailoring of material, design, and processing parameters. Validate model predictions against direct measurement using the Vickers microindentation method; (2) Experimentally quantify resistance to veneer chipping and fracture of porcelain- veneered prostheses with optimal material, design, and processing parameters relative to their bilayer counterparts and a commercial porcelain-fused-to-metal restoration, using edge-chipping methodology and mouth-motion fatigue testing. The approach is innovative because it departs from the status quo by developing a novel viscoelastic graded finite element method and utilizing this model to design continuously graded veneer/core interfaces. The proposed research is significant because it vertically advances the understanding of how stress profiles in all-ceramic prostheses can be tailored for better fracture resistance. Ultimately, such knowledge will bring us closer to a solution of a pervasive clinical problem?chipping, delamination and fracture of porcelain veneered prostheses?leading to reduced morbidity of dental prostheses and cost of replacement to the public.

Public Health Relevance

This new proposal aims to improve the resistance to chipping and fracture of porcelain-veneered zirconia and lithium disilicate dental prostheses through the design of a graded veneer/core interface and the optimization of material and processing parameters. This goal will be accomplished via the development of novel analytical viscoelastic graded finite elements and clinically-relevant testing methods. Knowledge generated from the study will open up new avenues for applications of advanced computational methods and material systems in health care, reduce morbidity and costs of dental restoration replacements, and improve public health and quality of life.

Agency
National Institute of Health (NIH)
Institute
National Institute of Dental & Craniofacial Research (NIDCR)
Type
Research Project (R01)
Project #
7R01DE026279-05
Application #
10273914
Study Section
Oral, Dental and Craniofacial Sciences Study Section (ODCS)
Program Officer
Lopez, Orlando
Project Start
2020-09-30
Project End
2022-07-31
Budget Start
2020-09-30
Budget End
2021-07-31
Support Year
5
Fiscal Year
2020
Total Cost
Indirect Cost
Name
University of Pennsylvania
Department
Dentistry
Type
Schools of Dentistry/Oral Hygn
DUNS #
042250712
City
Philadelphia
State
PA
Country
United States
Zip Code
19104
Zhao, M; Sun, Y; Zhang, J et al. (2018) Novel Translucent and Strong Submicron Alumina Ceramics for Dental Restorations. J Dent Res 97:289-295
Yan, Jing; Kaizer, Marina R; Zhang, Yu (2018) Load-bearing capacity of lithium disilicate and ultra-translucent zirconias. J Mech Behav Biomed Mater 88:170-175
Chai, Herzl; Mieleszko, Adam J; Chu, Stephen J et al. (2018) Using glass-graded zirconia to increase delamination growth resistance in porcelain/zirconia dental structures. Dent Mater 34:e8-e14
Mao, L; Kaizer, M R; Zhao, M et al. (2018) Graded Ultra-Translucent Zirconia (5Y-PSZ) for Strength and Functionalities. J Dent Res 97:1222-1228
Han, Aifang; Tsoi, James K H; Matinlinna, Jukka P et al. (2018) Effects of different sterilization methods on surface characteristics and biofilm formation on zirconia in vitro. Dent Mater 34:272-281
Kim, Jeongho; Dhital, Sukirti; Zhivago, Paul et al. (2018) Viscoelastic finite element analysis of residual stresses in porcelain-veneered zirconia dental crowns. J Mech Behav Biomed Mater 82:202-209
Souza, R; Barbosa, F; Araújo, G et al. (2018) Ultrathin Monolithic Zirconia Veneers: Reality or Future? Report of a Clinical Case and One-year Follow-up. Oper Dent 43:3-11
Zhang, Y; Lawn, B R (2018) Novel Zirconia Materials in Dentistry. J Dent Res 97:140-147
Figueiredo, Viviane Maria Gonçalves de; Pereira, Sarina Maciel Braga; Bressiani, Eduardo et al. (2017) Effects of porcelain thickness on the flexural strength and crack propagation in a bilayered zirconia system. J Appl Oral Sci 25:566-574
Stappert, Christian F J; Baldassarri, Marta; Zhang, Yu et al. (2012) Contact fatigue response of porcelain-veneered alumina model systems. J Biomed Mater Res B Appl Biomater 100:508-15