Improving mechanical properties and reducing internal stresses (induced by polymerization shrinkage) have been among the major research efforts for polymeric dental restorative composites for decades. The recently fast developing technology of """"""""electrospinning"""""""" and its novel product """"""""polymer nanofibers"""""""", provide a potential solution to solve these problems. Polymer nanofibers, with diameters ranging from several nanometers to several hundred nanometers, can be made from a variety of polymer solutions or melts. In the process of electrospinning, the key phenomenon """"""""bending instability"""""""" results in extremely large elongational flow rate of up to 1,000,000 s(-1). Such huge elongational flow rate can well align macromolecule chains as well as nanofillers (e.g., layered silicates) along the nanofiber axis; therefore, electrospun nanofibers can be extraordinary strong. The electrospun polymer nanofibers, typically collected as non-woven fabrics, can be soaked with and embedded into dental monomers (e.g., Bis-GMA/TEGDMA mixture). After polymerization, the composite resins are in the form similar to the interpenetration network (IPN). In this research, for the first time, the electrospun polymer nanofibers will be introduced to prepare dental materials. In particular, the use of strong nanofibers of Nylon 6 and/or Nylon 6/layered silicate nanocomposites (NLS) to improve the strength, and the use of elastomeric nanofibers of ethylene-propylene-diene elastomer (EPDM) to reduce the internal stresses, will be studied. Other objectives include (1) investigating the process of electrospinning to make nanofibers with desirable morphological and physical properties, (2) improving interfacial properties between the filler of nanofibers and the matrix resin, through both chemical modifications of the macromolecules and plasma surface treatment of the nanofibers, (3) evaluating hybrid embedding of Nylon 6, NLS and EPDM nanofibers to maximize strength, and to minimize internal stress, and (4) characterizing long-term mechanical and physical properties, such as wear, water aging and thermal cycling, for optimal composite resins with desirable properties (e.g. high strength and/or minimum internal stresses). This project will provide (1) the mechanisms of electrospun polymer nanofiber reinforcement and reduction of internal stress for dental resins; (2) guidelines on microstructural design and processing of nanofiber reinforced and/or toughened dental composite resins; and (3) a basis for the next generation of high performance composite resins for dental restorative (and potentially other biomedical) applications.

Agency
National Institute of Health (NIH)
Institute
National Institute of Dental & Craniofacial Research (NIDCR)
Type
Small Research Grants (R03)
Project #
5R03DE016042-02
Application #
6929352
Study Section
NIDCR Special Grants Review Committee (DSR)
Program Officer
Hunziker, Rosemarie
Project Start
2004-09-01
Project End
2007-08-31
Budget Start
2005-09-01
Budget End
2007-08-31
Support Year
2
Fiscal Year
2005
Total Cost
$65,650
Indirect Cost
Name
South Dakota School of Mines and Techn'Y
Department
Chemistry
Type
Schools of Arts and Sciences
DUNS #
929928018
City
Rapid City
State
SD
Country
United States
Zip Code
57701
Chen, Qi; Zhao, Yong; Wu, Weidong et al. (2012) Fabrication and evaluation of Bis-GMA/TEGDMA dental resins/composites containing halloysite nanotubes. Dent Mater 28:1071-9
Liao, Yiliang; Zhang, Lifeng; Gao, Yi et al. (2008) Preparation, characterization, and encapsulation/release studies of a composite nanofiber mat electrospun from an emulsion containing poly (lactic-co-glycolic acid). Polymer (Guildf) 49:5294-5299
Liu, Yi; Sagi, Sriramaraju; Chandrasekar, Ramya et al. (2008) Preparation and characterization of electrospun SiO2 nanofibers. J Nanosci Nanotechnol 8:1528-36
Tian, Ming; Gao, Yi; Liu, Yi et al. (2008) Fabrication and evaluation of Bis-GMA/TEGDMA dental resins/composites containing nano fibrillar silicate. Dent Mater 24:235-43
Liu, Yi; Cui, Li; Guan, Fangxiao et al. (2007) Crystalline Morphology and Polymorphic Phase Transitions in Electrospun Nylon 6 Nanofibers. Macromolecules 40:6283-6290
Tian, Ming; Gao, Yi; Liu, Yi et al. (2007) Bis-GMA/TEGDMA Dental Composites Reinforced with Electrospun Nylon 6 Nanocomposite Nanofibers Containing Highly Aligned Fibrillar Silicate Single Crystals. Polymer (Guildf) 48:2720-2728