The goals of this research are to establish criteria for damage occurring to articulating surfaces of total joint replacement components fabricated from ultra high molecular weight polyethylene (hereafter referred to simply as polyethylene) and to apply these criteria in optimizing implant design. Based on observations of retrieved implants and experimental and analytical determinations of the stresses occurring on and within components of contemporary total joint replacement designs, the following hypotheses specifically formulated to apply to knee joint geometry have been developed: Hypothesis 1: The type and extent of damage to the articulating surface of polyethylene joint components is directly related to the presence (sliding) or absence (rolling) of surface velocity of the mating component relative to the polyethylene. Hypothesis 2: The type and extent of damage to the articulating surface of polyethylene joint components is directly related to the geometry and conformity of the articulating surfaces and to the thickness of the polyethylene component. Hypothesis 3: The type and extent of damage to the articulating surface of polyethylene joint components is directly related to post manufacture treatments of the bulk polyethylene affecting consolidation, elastic modulus, and yield stress. To test these three hypotheses, an experimental loading apparatus will be used to examine the effect of single test variables on the damage occurring to polyethylene specimens. Observations and measurements made on the specimens will characterize the type and extent of damage sustained by the polyethylene. Results from finite element analyses will be used to establish appropriate specimen geometries and to correlate the observed damage with the predicted stress distributions in the specimens.

Agency
National Institute of Health (NIH)
Institute
National Institute of Arthritis and Musculoskeletal and Skin Diseases (NIAMS)
Type
Research Project (R01)
Project #
2R01AR038905-07A1
Application #
2079367
Study Section
Experimental Cardiovascular Sciences Study Section (ECS)
Project Start
1987-09-01
Project End
1997-06-30
Budget Start
1994-07-15
Budget End
1995-06-30
Support Year
7
Fiscal Year
1994
Total Cost
Indirect Cost
Name
Hospital for Special Surgery
Department
Type
DUNS #
City
New York
State
NY
Country
United States
Zip Code
10021
Estupinan, J A; Bartel, D L; Wright, T M (1998) Residual stresses in ultra-high molecular weight polyethylene loaded cyclically by a rigid moving indenter in nonconforming geometries. J Orthop Res 16:80-8
Astion, D J; Saluan, P; Stulberg, B N et al. (1996) The porous-coated anatomic total hip prosthesis: failure of the metal-backed acetabular component. J Bone Joint Surg Am 78:755-66
Pruitt, L; Koo, J; Rimnac, C M et al. (1995) Cyclic compressive loading results in fatigue cracks in ultra high molecular weight polyethylene. J Orthop Res 13:143-6
Elbert, K; Bartel, D; Wright, T (1995) The effect of conformity on stresses in dome-shaped polyethylene patellar components. Clin Orthop Relat Res :71-5
Elbert, K E; Wright, T M; Rimnac, C M et al. (1994) Fatigue crack propagation behavior of ultra high molecular weight polyethylene under mixed mode conditions. J Biomed Mater Res 28:181-7
Tsao, A; Mintz, L; McRae, C R et al. (1993) Failure of the porous-coated anatomic prosthesis in total knee arthroplasty due to severe polyethylene wear. J Bone Joint Surg Am 75:19-26
Wright, T M; Rimnac, C M; Stulberg, S D et al. (1992) Wear of polyethylene in total joint replacements. Observations from retrieved PCA knee implants. Clin Orthop Relat Res :126-34