Total joint replacement is an established method of treatment for severely impaired joints. However, significant complications exist which may limit the long-term success of total joint replacements. Several of these complications are associated with mechanical failure of ultra high molecular weight polyethylene, which may be affected by chemical degradation of the polyethylene. The purpose of this research is to determine the extent of chemical degradation occurring in polyethylene components in total joint arthroplasty. The degradation is affected by both the chemical environment and the loading history to which polyethylene is exposed in vivo. Chemical properties such as molecular weight and percent crystallinity are changed with time of implantation and there is an associated change in physical properties such as density and in mechanical properties such as elastic modulus. The dependence of the chemical, physical, and mechanical properties of polyethylene on degradation and loading history will be determined by exposing specimens to a fluid which simulates the in vivo environment, to cyclic loading, and to a combination of both as a function of time. The in vivo changes in the chemical and physical properties of polyethylene will be determined as a function of time and of location (in loaded and unloaded areas) in tibial components retrieved from a prospective study of total knee replacements. The course of degradation of mechanical properties for the retrieved tibial components will be predicted by performing a sequence of stress analyses in which the mechanical properties are varied as dictated by degradation and loading history utilizing the determined relationship between chemical and mechanical properties from the in vitro test. Parametric studies will then be performed to determine variations in stresses associated with degradation due to small changes in geometry of the femoral and tibial total knee components. The goal will be to determine the geometry which minimizes the effects of loading history on degradation and, therefore, improves the performance of polyethylene components while maintaining appropriate kinematic constraints for the total knee replacement.

Agency
National Institute of Health (NIH)
Institute
National Institute of Arthritis and Musculoskeletal and Skin Diseases (NIAMS)
Type
Research Project (R01)
Project #
5R01AR040191-03
Application #
3160508
Study Section
Orthopedics and Musculoskeletal Study Section (ORTH)
Project Start
1989-06-20
Project End
1994-05-31
Budget Start
1991-06-01
Budget End
1992-05-31
Support Year
3
Fiscal Year
1991
Total Cost
Indirect Cost
Name
Hospital for Special Surgery
Department
Type
DUNS #
City
New York
State
NY
Country
United States
Zip Code
10021
Kurtz, S M; Rimnac, C M; Bartel, D L (1998) Predictive model for tensile true stress-strain behavior of chemically and mechanically degraded ultrahigh molecular weight polyethylene. J Biomed Mater Res 43:241-8
Kurtz, S M; Bartel, D L; Rimnac, C M (1998) Postirradiation aging affects stress and strain in polyethylene components. Clin Orthop Relat Res :209-20
Kurtz, S M; Rimnac, C M; Bartel, D L (1997) Degradation rate of ultra-high molecular weight polyethylene. J Orthop Res 15:57-61
Astion, D J; Saluan, P; Stulberg, B N et al. (1996) The porous-coated anatomic total hip prosthesis: failure of the metal-backed acetabular component. J Bone Joint Surg Am 78:755-66
Kurtz, S M; Rimnac, C M; Santner, T J et al. (1996) Exponential model for the tensile true stress-strain behavior of as-irradiated and oxidatively degraded ultra high molecular weight polyethylene. J Orthop Res 14:755-61
Rimnac, C M; Klein, R W; Betts, F et al. (1994) Post-irradiation aging of ultra-high molecular weight polyethylene. J Bone Joint Surg Am 76:1052-6
Bostrom, M P; Bennett, A P; Rimnac, C M et al. (1994) The natural history of ultra high molecular weight polyethylene. Clin Orthop Relat Res :20-8